Precipitation hardening, also called age hardening or particle hardening, is a heat treatment technique used to increase the yield strength of malleable materials, including most structural alloys of aluminium, magnesium, nickel, titanium, and some steels, stainless steels, and duplex stainless steel. In superalloys, it is known to cause yield ...
As with most alloys, the melting point of stainless steel is expressed in the form of a range of temperatures, and not a single temperature. [9] This temperature range goes from 1,400 to 1,530 °C (2,550 to 2,790 °F; 1,670 to 1,800 K; 3,010 to 3,250 °R) [ 10 ] depending on the specific consistency of the alloy in question.
In 200 series stainless steels the structure is obtained by adding manganese and nitrogen, with a small amount of nickel content, making 200 series a cost-effective nickel-chromium austenitic type stainless steel. 300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless ...
Minimum design metal temperature. MDMT is one of the design conditions for pressure vessels engineering calculations, design and manufacturing according to the ASME Boilers and Pressure Vessels Code. Each pressure vessel that conforms to the ASME code has its own MDMT, and this temperature is stamped on the vessel nameplate. The precise ...
SAE Type 630 stainless steel (more commonly known as 17-4 PH, or simply 17-4; also known as UNS S17400) is a grade of martensitic precipitation hardened stainless steel. It contains approximately 15–17.5% chromium and 3–5% nickel, as well as 3–5% copper. [ 1] The name comes from the chemical makeup which is approximately 17% chromium and ...
Ferritic stainless steel[ 2][ 3] forms one of the five stainless steel families, the other four being austenitic, martensitic, duplex stainless steels, and precipitation hardened. [ 4] For example, many of AISI 400-series of stainless steels are ferritic steels. By comparison with austenitic types, these are less hardenable by cold working ...
The temperature range for process annealing ranges from 260 °C (500 °F) to 760 °C (1400 °F), depending on the alloy in question. This process is mainly suited for low-carbon steel. The material is heated up to a temperature just below the lower critical temperature of steel.
The main differences in composition, when compared with an austenitic stainless steel is that the duplex steels have a higher chromium content, 20–28%; higher molybdenum, up to 5%; lower nickel, up to 9% and 0.05–0.50% nitrogen.