Fatigue (material) Fracture surface of an aluminium crank arm from a bicycle. The dark area (due to oil, dirt and fretting) is a slow growth fatigue crack and may contain striations. The bright area is caused by sudden fracture. Mechanical failure modes. Buckling.
Corrosion fatigue is fatigue in a corrosive environment. It is the mechanical degradation of a material under the joint action of corrosion and cyclic loading. Nearly all engineering structures experience some form of alternating stress, and are exposed to harmful environments during their service life. The environment plays a significant role ...
The fatigue limit or endurance limit is the stress level below which an infinite number of loading cycles can be applied to a material without causing fatigue failure. [ 1] Some metals such as ferrous alloys and titanium alloys have a distinct limit, [ 2] whereas others such as aluminium and copper do not and will eventually fail even from ...
Corrosion is a natural process that converts a refined metal into a more chemically stable oxide. It is the gradual deterioration of materials (usually a metal) by chemical or electrochemical reaction with their environment. Corrosion engineering is the field dedicated to controlling and preventing corrosion. [ 1][ 2]
Metal fatigue occurs when metal - including parts in machines, vehicles and structures - sustains microscopic cracks after being exposed to repeated stress or motion, damage that tends to worsen ...
In the mechanics of materials, the strength of a material is its ability to withstand an applied load without failure or plastic deformation. The field of strength of materials deals with forces and deformations that result from their acting on a material. A load applied to a mechanical member will induce internal forces within the member ...
Stress corrosion cracking ( SCC) is the growth of crack formation in a corrosive environment. It can lead to unexpected and sudden failure of normally ductile metal alloys subjected to a tensile stress, especially at elevated temperature. SCC is highly chemically specific in that certain alloys are likely to undergo SCC only when exposed to a ...
In metallurgy and materials science, annealing is a heat treatment that alters the physical and sometimes chemical properties of a material to increase its ductility and reduce its hardness, making it more workable. It involves heating a material above its recrystallization temperature, maintaining a suitable temperature for an appropriate ...